Радиационное дефектообразование в кристаллах KCl

Authors

  • И Нуритдинов

    Institute of Nuclear Physics of the Uzbekistan Academy of Sciences

  • М.А Муссаева

    Institute of Nuclear Physics of the Uzbekistan Academy of Sciences

  • Д.П Юлдашов

    Institute of Nuclear Physics of the Uzbekistan Academy of Sciences

  • Б.Т Аташов

    Nukus State Pedagogical Institute named after Ajiniyaz image/svg+xml

Keywords: potassium chloride (KCl), X-ray irradiation, absorption spectra, color centers

Abstract

This work presents the results of studying radiation-induced defect formation in KCl crystals exposed to X-ray and gamma irradiation. It is shown that F-centers begin to form from the early stages of irradiation and reach saturation at doses of about 100 rad. At higher doses (Dγ ≥ 10⁵ rad), absorption bands corresponding to I- and V-centers appear, indicating the formation of new structural defects. The mechanisms of creation and stabilization of these defects are analyzed.

References

1. Алукер Э.Д., Лусис Д.Ю., Чернов С.А. Электронные возбуждения и радиолюминесценция щелочно-галоидных кристаллов. Зинатне: – Рига: 1979.

2. Кудрявцева И.А., Василченко Е.А., Лущик А.Ч., Лущик Ч.Б. Образование и стабилизация F- центров после прямого создания автолокализованных экситонов в кристаллах KCL. // ФТТ, 1999, Т. 41, вып.3. – С. 433-447.

3. Лущик Ч.Б., Лущик А.Ч., Лущик Ч.Б. Распад электронных возбуждений с образованием дефектов в твердых телах. – Москва: «Наука», 1989.